STUDY OF COATINGS OBTAINED FROM ALLOY Fe-Mn-C-B-Si-Ni-Cr
Mychajło Paszeczko 1  
,  
Krzysztof Dziedzic 1  
,  
 
 
More details
Hide details
1
Faculty of Fundamentals of Technology, Lublin University of Technology, Nadbystrzycka 38 Str., 20-618 Lublin, Poland
CORRESPONDING AUTHOR
Marcin Barszcz   

Lublin University of Technology, Nadbystrzycka 38, 20-615 Lublin, Poland
Publish date: 2016-09-01
 
Adv. Sci. Technol. Res. J. 2016; 10(31):194–198
KEYWORDS
TOPICS
ABSTRACT
Tribological behaviour of coatings obtained from eutectic alloy Fe-Mn-C-B-Si-Ni-Cr was studied. The coatings were obtained by the method of gas metal arc welding (GMA) with use of powder wire. GMA welding method is widely used for the regeneration of machine parts. Eutectic Fe-Mn-C-B-Si-Ni-Cr alloys can be used to obtain high quality coatings resistant to wear and corrosion. Pin-on-disk dry sliding wear tests at sliding speeds 0.4 m/s and under load 10 MPa were conducted for pin specimens. During friction a typical tribological behavior was observed. The mechanism of wear was mechanical-chemical.