THE SURFACE STRUCTURAL AND MECHANICAL PROPERTIES OF THE AMORPHOUS CO22Y54AL24 RIBBON
More details
Hide details
1
Institute of Materials Science and Engineering. Department of Materials Processing Technology and Applied Physics, Częstochowa University of Technology, 19 Armii Krajowej Str., 42-200 Częstochowa, Poland
2
Institute of Physics. Department of Materials Processing Technology and Applied Physics, Częstochowa University of Technology, 19 Armii Krajowej Str., 42-200 Częstochowa, Poland
Publication date: 2013-09-06
Adv. Sci. Technol. Res. J. 2013; 7(19):1-4
KEYWORDS
ABSTRACT
The aim of this study was to manufacture amorphous Co22Y54Al24 alloy in a form of thin ribbons and to investigate their properties. The investigated ribbons were prepared by rapid solidification of molten metal on a rotating copper cylinder (melt-spinning). In order to obtain the material with amorphous structure, the cooling rate of the liquid alloy should vary in a range from 104 to 106 K/s. The microstructure studies were performed using X-ray diffractometery. The mechanical properties were investigated by metallographic studies, micro-hardness and tribological resistance tests moreover the surface roughness profile were analyzed. All studies were performed for two sides of tapes, since the differences in ribbons surface, related with manufacturing process, are clearly visible. The surface from the bottom (drum side) was glossy and from the top side it was shiny.