Features of Formation Stress State of Amorphized Detonation Coatings of the Zr-Al-B Systems
 
Więcej
Ukryj
1
Department of Fundamentals of Technology, Lublin University of Technology, Nadbystrzycka 38, 20-618 Lublin, Poland
 
2
Airport technology department, National Aviation University, ave. Kosmonavta Komarova, 1, Kiev, 03067, Ukraine
 
3
Institut of Engineering Thermophysics of National Academy of Scinces of Ukraine, Kiev, Ukraine
 
4
Khmelnitskee National university, Mailing str. Institutskaya, 11, Khmelnitskee-16, 29016, Ukraine
 
 
Data publikacji: 01-06-2019
 
 
Autor do korespondencji
Mykhaylo Pashechko   

Department of Fundamentals of Technology, Lublin University of Technology, Nadbystrzycka 38, 20-618 Lublin, Poland
 
 
Adv. Sci. Technol. Res. J. 2019; 13(2):46-50
 
SŁOWA KLUCZOWE
DZIEDZINY
 
STRESZCZENIE
The results of experimental studies of the dependence of the thickness of amorphous-crystalline Zr-Al-B coatings on the value and level of distribution of residual stresses of type 1 are presented. Was demonstrated that residual compressive stresses arise in the surface layers of coatings, which in absolute value are not significant for its integrity and quality. It is established that the amorphous-crystalline composition, in conditions of minimizing residual stresses and the optimal combination of the volume fraction of components, the structure and morphology of their components, has the best surface strength and wear resistance under friction compared to tungsten carbide and iron coatings