PROPERTIES OF ORGANIC COATINGS CONTAINING PIGMENTS WITH SURFACE MODIFIED WITH A LAYER OF ZnFe2O4
 
Więcej
Ukryj
1
Faculty of Chemical Technology, Institute of Chemistry and Technology of Macfromolecular Materials, University of Pardubice, Studentská 95, 53210 Pardubice, Czech Republic
 
 
Data publikacji: 27-11-2015
 
 
Adv. Sci. Technol. Res. J. 2015; 9(28):51-55
 
SŁOWA KLUCZOWE
STRESZCZENIE
This work is focussed on the properties of organic coatings containing pigments whose surface was chemically coated with zinc ferrite (ZnFe2O4) layer. Four silicate types with different particle shapes were selected as the cores: diatomite, talc, kaolin and wollastonite. The untreated particles exhibit a barrier effect. The aim of this project was to apply the surface treatment approach with a view to enhancing not only the model paint films’ anticorrosion properties but also their resistance to physico- mechanical tests pursuant to ISO standards (cupping, bending, impact, adhesion). Other parameters examined included: particle size and morphology, density of the modified pigment, oil consumption, pH, conductivity, and electrochemical properties of the paint film. A solvent-based epoxy-ester resin was used as the binder and also served as the reference material. The pigment volume concentration (PVC) was 1% and 10%. During the last stage of the experiment, the paint films were exposed to a corrosive environment stimulating seaside conditions or conditions roads treated with rock salt. The accelerated cyclic corrosion test in a neutral salt mist atmosphere was conducted for 864 hours. The results served to ascertain a suitable environment for organic coatings.
 
REFERENCJE (13)
1.
Singh S., Kumar N., Bhargava R., Sahni M., Sung K., Jung J.H. Magnatodielectric effect in BaTiO3/ZnFe2O4 core/shell nanoparticles. Journal of Alloys and Compounds, 587, 2014, 437–441.
 
2.
Cunha I.T. et al. Catalytic oxidation of aqueous sulfide in the presence of ferrites (MFe2O4, M = Fe, Cu, Co). Catal. Today, 2015 (article in press).
 
3.
Miszcyk A., Darowicki K. Study of antocorrosion and microwave absorption properties of NiZn ferrite pigments. Anti-Corrosion Methods and Materials, 58, 2011, 13–21.
 
4.
Kalendová A., Ryšánek P., Nechvílová K. Investigation of the anticorrosion efficiency of ferrites Mg1-xZnFe2O4 with different particle morphology and chemical composition in epoxy-ester resin-based coatings. Progress in Organic Coatings, 86, 2015, 147–163.
 
5.
Chaudhry A.U., Mittal V., Mishra B. Nano nickel ferrite (NiFe2O4) as anti-corrosion pigment for API 5L X-80 steel: An electrochemical study in acidic and saline media. Dyes snd Pigments, 158, 2015, 18–26.
 
6.
Liu Y., Wei S., Tong H., Tian H., Liu M. Corrosion behavior of marnetic ferrite coating prepares by plasma spraying. Materials Research Bulletin, 60, 2014, 359–366.
 
7.
Chromy L., Kaminska E. Non-toxic anticorrosive pigments. Progress in Organic Coatings, 18, 1990, 319–324.
 
8.
Dondi M., Zanelli C., Ardit M., Cruciani G., Mantovani L., Tribaudino M., Andreozzi G.B., Ni-free. black ceramic pigments based on Co-Cr-Fe-Mn spinels: A reappraisal of crystal structure. color and technological behavior. Ceramics International, 39, 2013, 9533–9547.
 
9.
Kalendová A. Alkalisong and neutralising effects of anticorrosive pigments containing Zn, Mg, Ca and Sr catoins. Progress in Organic Coatings, 38, 2000, 199–206.
 
10.
Brodinová J., Stejskal J., Kalendová A., Investigation of ferrites properties with polyaniline layer in anticorrosive pigments. Journal of Physics and Chemistry of Solids, 68, 2007, 1091–1095.
 
11.
Hayyan M., Sameh S.A., Hayyan A., Al Nashef I.M. Utilizing of sodium nitrate as inhibitor for protection of carbon steel in salt solution. International Journal of Electrochemical Science, 7, 2012, 6941–6950.
 
12.
Zhu Y.D., Allen G.C., Adams J.M., Gittins D.I., Hooper J.J., Skuse D.R. Barrier properties of latex/kaolin coatings. Polymer Chemistry, 16, 2013, 4386–4395.
 
13.
Behler K.D., Stravato A., Mochalin V., Korneva G., Yushin G., Gofotsi Y. Nanodiamond-Polyymer Composite Fibres and Coating, ACS Nano, 3, 2009, 363–369.
 
Journals System - logo
Scroll to top