Factors Influencing Cavitation Erosion of NiCrSiB Hardfacings Deposited by Oxy-Acetylene Powder Welding on Grey Cast Iron
 
Więcej
Ukryj
1
Department of Materials Engineering, Mechanical Engineering Faculty, Lublin University of Technology, Poland
AUTOR DO KORESPONDENCJI
Mirosław Szala   

Department of Materials Engineering, Mechanical Engineering Faculty, Lublin University of Technology, Poland
Data publikacji: 01-12-2021
 
Adv. Sci. Technol. Res. J. 2021; 15(4):376–386
 
SŁOWA KLUCZOWE
DZIEDZINY
 
STRESZCZENIE
The work presents the results of a study on cavitation erosion (CE) resistance of two NiCrSiB self-fluxing powders deposited by oxy-acetylene powder welding on cast iron substrate grade EN-GJL-200. The mean hardness of deposits A-NiCrSiB, C-NiCrSiB is equal to 908 HV, 399 HV and exceeds those of EN-GJL-200 and X5CrNi18-10 reference specimens 197 HV and 209 HV, respectively. To study CE, the vibratory apparatus has been used and tests were conducted according to the ASTM G32 standard. Cavitation eroded surfaces were examined using a profilometer, optical and scanning electron microscopy. The research indicated that the CE resistance, expressed by the cumulative mass loss decreased in the following order C-NiCrSiB > A-NiCrSiB > X5CrNi18-10 > EN-GJL-200. Therefore, hardfacings were characterised by lower cumulative mass loss, in turn, higher CE resistance than the reference sample and therefore they may be applied as layers to increase resistance to cavitation of cast iron machine components. Results indicate that in the case of multiphase materials, hardness cannot be the main indicator for CE damage prediction while it strongly depends on the initial material microstructure. To qualitatively estimate the cavitation erosion damage (CEd) of NiCrSiB self-fluxing alloys at a specific test time, the following factors should be considered: material microstructure, physical and mechanical properties as well as surface morphology and material loss both estimated at specific exposure time. A general formula for the CEd prediction of NiCrSiB deposits was proposed.